DRYING OF CALCIUM SULPHATE SLURRY

(Chemistry)

DRYING OF CALCIUM SULPHATE SLURRY

ABSTRACT

Drying is a unit operation that is employed to calcuim sulphate slurries in order to remove or reduce the content of the liquid to an acceptable low value.  The liquid content of a dried calcium sulphate varies from product to product.

The experiment was carried out in the ceramic laboratory where the same quantity of plaster of paris (P.O.P) where measured out and mix thoroughly with specific amount of water.  It was stirred continuously so as to form a shry.  We prepared seven different samples but of the same quantity of plastic of paris (P.O.P) and water and then, was place inside a dryer )Oven) in which the samples derived with different time because of the different in temperatures.

The material was weighed before drying and after drying which helped us to know the constant rate period. W e make sure all the samples reaches the constant rate period.

TABLE OF CONTENTS

CHAPTER ONE

INTRODUCTION                                                     

CHAPTER TWO

LITERATURE REVIEW                             

CHAPTER THREE

ANALYSIS / PROCEDURE                                  

CHAPTER FOUR

DISCUSSION                                                                      

CHAPTER FIVE

CONCLUSION / RECOMMENDATION                          

APPENDIX

REFERENCE                                                                      

CHAPTER ONE

INTRODUCTION

Calcium sulphate hemi hydrate as it is called has a chemical formula (CaS04 ½ H2O). Calcuim sulphate is made from mineral gypsum with chemical formula (CaSO4 2H2O)

The material gypsum is of fairly widely occurrence almost pure and wide various impurities which colour it and modify the properties of the plasters of paris (POP) made from it

DIFFERENCES IN CHEMICAL FORMULA

The slight difference in chemical formula of the mineral gypsum and plaster of paris (P.O.P) is half molecule of water crystallization thus.  Crypsum caso42H20 M.W 172. 18 Calcium sulphate 79.1% H2O 20. 19% Plaster of paris (POP) Caso4 ½ H2O M.W 154. 16 CaSoO4  93.8% H2O 6.2% Anhydrous caso4 M.W 136.15 Calcium sulphate (Caso4) 100% Successful production of calcium sulphate from gypsum is complicated by the number of possible dehydration product.

                        TYPES OF HEMIHYDRATES

Theme are two hemihydrates & and B. the & form markes much stronger and generally more satisfactory plaster and is therefore the desired dehydration product.

TYPES OF ANHYDROUS CALCUIM SULPHATE

There are also four types of anhydrous calcium sulphate obtained by stronger heating of gypsum.

The & hemihydrate forms by recrystallization of gypsum from water above 1150C (239of) it’s formation is therefore favoured by heating gypsum in a sufficiently damp atmosphere for there to be a thin absorbed water layer on the particle B – hemihydrat is formed when gypsum is heated rapidly in dry atmosphere above 1000C (2120f), On heating ground gypsum the temperature rises until 120‑C (2620f) when violent boiling occurs.  The temperature does not rise again until this has ceased and the plaster enters the first settle, on further heating a second sharter period of boiting begins at 1630C (32.0f) after which plaster enters the “second settle”.

On continued further heating the hemihydrate begins to decompose, giving off water and being converted into the anhydrous salt at 800 – 10000C (1470-18300f) the dead Bioned gypsum or keene’s cement is attained.

First settle plaster is more plastic and easier to work than second settle material.  The later, however gives a denser and stronger set.

TERMS AND CONDITIONS

Using our service is LEGAL and IS NOT prohibited by any university/college policies

You are allowed to use the original model papers you will receive in the following ways:

1. As a source for additional understanding of the subject

2. As a source for ideas for your own research (if properly referenced)

3. For PROPER paraphrasing (see your university definition of plagiarism and acceptable paraphrase)

4. Direct citing (if referenced properly)

Thank you so much for your respect to the authors copyright.

For more project materials

Log on to www.grossarchive.com

Or call

+2348130686500

+2348093423853

500
Leave a comment...

    Project Details

    Department Chemistry
    Project ID CHM0008
    Price N3000 ($14)
    CHAPTERS 5 Chapters
    No of Pages 39 Pages
    Methodology Scientific Method
    Reference YES
    Format Microsoft Word

    Related Topics