Synthesis And Characterization Of Nanocalcium Titanate (Perovskite)

  • Type:Project
  • Pages:39
  • Format:Microsoft Word
(Material Science Project Topics & Materials)
ABSTRACT
According to a few recent studies, calcium titanate is a material that is similar to hydroxyapatite in biological properties. However, calcium titanate is not currently being used in the biomedical application as to hydroxyapatite. The objective is to prepare nano calcium titanate powder from the solution of calcium oxide, ethanol, and titanium (IV) isopropoxide via sol-gel synthesis. The fiber size, pore size and morphology were studied by phenom scanning electron microscope (SEM). The results of the uniformity in the pore size histogram confirm the presence of phase pure crystalline CaTiO3 after drying at 100oC for 24 hours, while the fiber analysis confirms the CaTiO3 to be a nano material. The phase analysis shows the morphology of the nano calcium titanate at different magnification. Finally, it can be concluded that sol-gel synthesis is a good method for production of nano CaTiO3 particles at lower temperature compared to any other methods of production.
 
TABLE OF CONTENT

CHAPTER ONE
1.0 Introduction _________________________ 1
1.1 Aim   ______________________________ 2
1.2 Objectives ______________________________ 2  
1.3 Justification of the study ____________________ 3
1.4 Scope of the study ____________________ 3

CHAPTER TWO
2.0 Literature review ____________________ 4
2.1 Methods of synthesis ____________________ 5
2.1.1 Ceramic method ____________________ 5
2.1.2 Sol-gel method ____________________ 6
2.1.3 Freeze-drying method ____________________ 6
2.1.4 Melt method _________________________ 7
2.1.5 Pechini method _________________________ 8
2.1.6 Other methods _________________________ 8
2.2 Structure of calcium titanate _______________ 10
2.3 Structural characterization of perovskite _____ 12
2.3.1 X-ray diffraction __________________________ 14
2.3.2 Scanning electron microscopy ________________ 16
2.4 Applications __________________________ 17

CHAPTER THREE
3.0 Materials and method _____________________ 19
3.1 Preparation of titanium (IV) isopropoxide ______ 19
3.2 Powder synthesis __________________________ 19
3.3 Powder characterization _____________________ 20

CHAPTER FOUR
4.0 Result __________________________ 21

CHAPTER FIVE
5.0 Discussion, Conclusion and Recommendation 30
5.1 Discussion __________________________ 30
5.2 Conclusion __________________________ 32
5.3 Recommendation _____________________ 32
Reference __________________________ 33
LIST OF FIGURES

Figure 1 SEM Microgram of CaTiO3 __________ 21
Figure 2 SEM Microgram of CaTiO3 __________ 22
Figure 3 SEM Microgram of CaTiO3 __________ 23
Figure 4 SEM Microgram of CaTiO3 __________ 24
Figure 5 A screen shot of SEM fibre and pore analysis 25
Figure 6 Fibermetric image of SEM analysis _____ 26
Figure 7 Fibermetric image measurement of SEM analysis 27
Figure 8 Fiber histogram of SEM analysis _____ 28
Figure 9 Pore histogram of SEM analysis _____ 29


Synthesis And Characterization Of Nanocalcium Titanate (Perovskite)

Share This

Details

Type Project
Department Material Science
Project ID MCI0005
Price ₦3,000 ($9)
No of Pages 39 Pages
Format Microsoft Word

500
Leave a comment...

    Details

    Type Project
    Department Material Science
    Project ID MCI0005
    Price ₦3,000 ($9)
    No of Pages 39 Pages
    Format Microsoft Word

    Related Works

    ABSTRACT According to a few recent studies, calcium titanate is a material that is similar to hydroxyapatite in biological properties. However, calcium titanate is not currently being used in the biomedical application as to hydroxyapatite. The objective is to prepare nano calcium titanate powder from the solution of calcium oxide, ethanol, and... Continue Reading
    Metal complexes are scientifically known to be active and effective as antibacterial, antivirus and some antifungal etc. This project work is targeted at preparing complex from transition metals say; cobalt, cupper, zinc and nickel and organic ligands synthesised from pyridyl based schiff bases, one from 2-aminopyridine and benzaldehyde and second... Continue Reading
    ABSTRACT The present paper describes the synthesis of Acid Orange(7)dye which can be used as dyes for cellulose acetate biopolymer. They were obtained by the diazotization of a monoazo component of the mono-azobenzene type, followed by coupling. The monoazo components were obtained by the diazotization of sulphanilic acid and coupling with... Continue Reading
    Mechanochemical synthesis of [Cu(OOCCH3)2(THB)2] and theMechanochemical synthesis of [Cu(OOCCH3)2(THB)2] were carried out, and a brown solid complexes obtained in both experiment was washed in ethanol respectively. The physical and instrumental characterisation of the complexes carried out revealed that the complexes obtained are the same... Continue Reading
    ABSTRACT The strategy of utilizing mechanochemical synthesis to obtain metal-organic frameworks with high surface area and nanodisperse particles has been espoused. Transition metal ions have been shown to form complexes with organic moieties such as benzyl-N,N-dimethyldithiocarbamate. It has been established that iron in its oxidised state (Fe 3+... Continue Reading
    SYNTHESIS AND 1 HNMR CHARACTERIZATION OF Co(II) AND Fe(II) COMPLEXES OF MIXED SCHIFF BASE LIGAND DERIVED FROM SALICYLALDEHYDE AND 2-HYDROXY-1-NAPHTHALDEHYDE WITH 2-AMINOPHENOL A RESEARCH PROJECT BY NKEMJIKA, EMMANUEL EKE 12/SC/CH/256 SUBMITTED TO DEPARTMENT OF CHEMISTRY FACULTY OF SCIENCE UNIVERSITY OF UYO, UYO AKWA IBOM STATE IN PARTIAL... Continue Reading
    SYNTHESIS AND 1 HNMR CHARACTERIZATION OF Co(II) AND Fe(II) COMPLEXES OF MIXED SCHIFF BASE LIGAND DERIVED FROM SALICYLALDEHYDE AND 2-HYDROXY-1-NAPHTHALDEHYDE WITH 2-AMINOPHENOL A RESEARCH PROJECT BY NKEMJIKA, EMMANUEL EKE 12/SC/CH/256 SUBMITTED TO DEPARTMENT OF CHEMISTRY FACULTY OF SCIENCE UNIVERSITY OF UYO, UYO AKWA IBOM STATE IN PARTIAL... Continue Reading
    ABSTRACT Nickel amine carboxylate complexes were synthesized by reacting Ni(ii)chloride with ammonia, malonic and tartaric acid, which formed Nickel amine malonate and Nickel amine tartarate  of  blue and green crystal and  the percentage yield are of both complexes are 62.65% and 62.83% respectively. The decomposition temperatures were 218o C... Continue Reading
    ABSTRACT This thesis aimed at the production of biolubricant from vegetable oils. The first stage produced methyl ester of the oil and in the second stage; the methyl ester was transesterified with Trimethylolpropane (TMP) in a ratio of 3.5:1 at 1500C to produce the biolubricant. The pour points biolubricant and its blend were significantly... Continue Reading
    ABSTRACT This project was carried out using coal sample from Onyeama coal mine Enugu, Enugu State.Activated coal was produced by carbonizing the coal and activating it using phosphoric acid at a temperature of 5500c. the degree of bleaching of raw palm oil was monitored using spectronic meter through absorbance measurement. The essence was to... Continue Reading